GX120Mn12|K700|1.3401
High manganese steel K700的一个含锰12-14%和1.2 -1.4%碳合金High manganese steel。
The 10:1 ratio of manganese to carbon content following rapid quenching in water after solution heat treatment at 1000 to 1100 o C, fully retains its austenitic structure at room temperature.
锰的比例为10:1的碳含量在水中的快速解决方案, 在 1000到1100摄氏度热处理淬火后,充分保留了其在室温下的奥氏体结构。 The unique process of cross rolling produces a supreme uniformity in terms of mechanical - technological and physical properties.
独特的横轧过程中产生的在机械方面的 均匀度 - 技术和物理性能。 This special wear resisting hard manganese steel features high toughness and excellent weldability which acquires its working hardness (surface up to 600 BHN) by strain hardening, thus being particularly suited for applications involving wear by impact or pressure.
这种特殊的耐磨硬锰钢,具有高韧性和优良的焊接性能,获得其工作应变硬化的硬度 (表面600 BHN),涉及影响或压力的磨损的应用,特别适合.
---------高高特钢:021-56103917---何云飞---24咨询13585717556------------

-------QQ:694992782-----上海宝山区抚远路1288弄61---------

          T:029-88661877  13324526777
高高特钢分部:西 安 冠 玥    西安 特钢         
------------------------------------
 K700 - Manganese wear resistant steel
锰耐磨钢 C 彗星 Si 四 Mn 锰 Typical Analysis
典型分析 (Ave. values %) (Ave.值%) 1.23 1.23 0.40 0.40 12.50 12.50 DIN DIN AFNOR AFNOR UNI UNI的 NEAREST
附近 STANDARD 标准 1.3401 1.3401 X120Mn12 X120Mn12 Z120M12 Z120M12 GX 120 Mn 12 GX 120锰12 DESCRIPTION
描述 Special wear resistant manganese steel featuring high toughness and excellent
特别耐磨锰钢,具有高韧性和优良的 weldability which acquires its working hardness (surface up to 600 BH) by strain
可焊性收购的应变其工作硬度(表面高达600波黑) hardening, thus being particularly suited for applications involving wear by impact or 硬化,因而特别适合于涉及冲击磨损的应用程序或 pressure. 压力。 APPLICATIONS 应用 Various components for crushing, bulk material handling, ore dressing and processing 破碎,散装物料输送,选矿和加工的各个组成部分 equipment such as crusher jaws, impact bars, impact plates, hammers, liners, 设备,如颚式破碎机,冲击酒吧,冲击板,锤,衬垫, elevator buckets, dredger teeth, bucket links, track rollers, armour plate for safes, 电梯桶,挖泥船牙齿,斗链接,滚轮,装甲钢板保险箱, reinforcement panels for strong rooms, jail bars, railway rolling stock axel box liners. 强烈室,监狱酒吧,铁路机车车辆阿克塞尔盒内衬加固板。 HEAT 热 TREATMENT 治疗 Quenching temperature 淬火温度 1000-1050 Water 1000-1050水 Tensile 拉伸 Strength 强度 MPa 兆帕 Yield 产量 Strength 强度 MPa 兆帕 Elong. 艺龙。 % % Red of 红色 area 区 Izod 悬臂梁 Impact 影响 J J Brinell 布氏 Hardness 硬度 800-1000 800-1000 ≥ 350 ≥350 >35 > 35 >35100200 > 35100200 MECHANICAL 机械 PROPERTIES 性能 Quenched 淬火 K700 obtains its characteristic properties by work hardening under impact and K700的冲击下获得的特征属性和加工硬化 compressive stresses and it is not comparable with other hardenable steels. 压应力,它不与其他可比硬化钢。 Density 密度 kg/dm 公斤/ DM 3 3 7.90 7.90 Modulus of elasticity 弹性模量 10 10 3 3 N/mm 牛顿/毫米 2 2 190 190 Thermal conductivity 导热系数 W/(mK) W /(MK) 13 13 Electric resistivity 电阻率 2 2 /m / M 0.68 0.68 Specific heat capacity 比热容 J/(kg.K) J /(kg.K) 500 500 PHYSICAL 物理 PROPERTIES 性能 Thermal expansion 热膨胀系数 10 10 6 6 m/(mK) 米/(MK) 18.2 18.2